Specification for 24/17 chromium-nickel heat-resisting steel sheet and strip (titanium stabilized: 540 MPa) (elevated temperature properties not verified)
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.12 | ||
| Si | 0.20 | 1.00 | ||
| Mn | 0.50 | 2.00 | ||
| P | - | 0.035 | ||
| S | - | 0.025 | ||
| Cr | 23.00 | 26.00 | ||
| Ni | 16.00 | 19.00 | ||
| Mo | - | - | ||
| Ti | 5×C | 0.90 |
Specification for 24/17 chromium-nickel heat-resisting steel sheet and strip (titanium stabilized: 540 MPa) (elevated temperature properties not verified)
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 856 (≥) | 446 (≥) | 31 | 23 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 412 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 898 (≥) | 173 (≥) | 43 | 24 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 113 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 179 | 985 | 678 |
We can customize the production of S.530 grade, contact us for the best solution.