Martensitic Stainless Steel (Hardenable by Heat Treatment)
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.15 | ||
| Mn | - | 1.00 | ||
| Si | - | 0.50 | ||
| P | - | 0.04 | ||
| S | - | 0.03 | ||
| Cr | 11.50 | 13.00 | ||
| Ni | - | - | ||
| Mo | - | - |
Martensitic Stainless Steel (Hardenable by Heat Treatment)
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 913 (≥) | 673 (≥) | 31 | 43 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 422 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 365 (≥) | 596 (≥) | 43 | 11 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 112 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 325 | 952 | 324 |
We can customize the production of S40300 grade, contact us for the best solution.