Stainless steel blooms and billets for forgings
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.08 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.045 | ||
| S | - | 0.030 | ||
| Cr | 17.00 | 19.00 | ||
| Ni | 9.00 | 13.00 | ||
| Mo | - | - | ||
| N | - | - | ||
| Ti | 5×C％ | - |
Stainless steel blooms and billets for forgings
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 257 (≥) | 973 (≥) | 31 | 41 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 211 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 366 (≥) | 149 (≥) | 43 | 41 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 421 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 529 | 882 | 526 |
We can customize the production of STS321HFB grade, contact us for the best solution.