Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | - | 0.08 | ||
Si | 0.50 | 1.00 | ||
Mn | 1.00 | 2.00 | ||
P | - | 0.035 | ||
S | - | 0.020 | ||
Cr | 18.50 | 20.50 | ||
Ni | 10.00 | 13.00 | ||
Mo | - | 0.30 | ||
Nb | 0.80 | 1.10 | ||
V | 1.00 | 1.30 | ||
N | 0.10 | 0.20 |
Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
957 (≥) | 593 (≥) | 24 | 44 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 144 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
283 (≥) | 366 (≥) | 32 | 22 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 421 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
618 | 542 | 632 |
We can customize the production of 08X19H12TΦ grade, contact us for the best solution.