Heat-treatable steels, alloy steels and free-cutting steels -- Part 15: Valve steels for internal combustion engines
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.10 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.030 | ||
| S | - | 0.015 | ||
| Cr | 18.00 | 21.00 | ||
| Mo | - | - | ||
| Ni | remaining | - | ||
| Al | 0.30 | 1.00 | ||
| Fe | 23.00 | 28.00 | ||
| Nb+Ta | 1.00 | 2.00 | ||
| B | - | 0.008 |
Heat-treatable steels, alloy steels and free-cutting steels -- Part 15: Valve steels for internal combustion engines
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 415 (≥) | 121 (≥) | 33 | 24 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 221 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 687 (≥) | 159 (≥) | 31 | 34 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 217 | 118 | 848 |