Nickel 200 Superalloys to ASTM B160
Nickel 200 - Specification & Application
- ASTM B160 - Bars
- ASTM B162 - Plates
- BS 3075 NA11 -
- BS 3076 NA11 -
- ASTM B564 - Forged pieces
Acid or alkaline food production (fruit juices, ice-creams), cristallization and concentration of mineral salts. Concentration of caustic salts. Machineries in which hydrocarbons are in reaction with fluorides. Storing and carriage of phenol. Production o
Chemical composition(wt.%) of Nickel 200 grade: to ASTM B160
| Elements |
Min.（≥） |
Max.（≤） |
Similar |
Remarks |
| C |
- |
0.15 |
|
|
| Si |
- |
0.35 |
|
|
| Mn |
- |
0.35 |
|
|
| S |
- |
0.01 |
|
|
| Ni |
99 |
- |
|
|
| Cu |
- |
0.25 |
|
|
| Fe |
- |
0.40 |
|
|
| Mg |
- |
0.20 |
|
|
| Ti |
- |
0.10 |
|
|
| Co |
- |
2.00 |
|
|
Mechanical properties of grade Nickel 200 grade: to ASTM B160
Yield Strength,Rp 0.2(MPa)
| Condition |
Min |
Max |
Similar |
Note |
| ASTM B160 - 93 |
415 |
|
|
|
Tensile Strength,Rm(MPa)
| Condition |
Min |
Max |
Similar |
Note |
| ASTM B160 - 93 |
550 |
|
|
|
Impact,Kv/Ku(J)
| Condition |
Min |
Max |
Similar |
Note |
Elongation,A(%)
| Condition |
Min |
Max |
Similar |
Note |
| ASTM B160 - 93 |
10 |
|
|
|
Reduction of area,(%)
| Condition |
Min |
Max |
Similar |
Note |
Hardness
| Condition |
Type |
Min |
Max |
Similar |
Note |
Related properties
| Density - 8.89 |
| Melting Point - 1446°C |
| Coefficient of Expansion - 13.3 μm/m °C (20 – 100°C) |
| Modulus of Rigidity - 81 kN/mm² |
| Modulus of Elasticity - 204 kN/mm² |
| Electrical Resistivity - 9.6 μΩ • cm |
| Thermal Conductivity - 70.2 W/m • °C |
| Forging conditions - Forging is made at a range of temperature included between 1150 and 950°C, then cooled at appropriate conditions for the final thermal treatment and obtain required characteristics. In any case, please contact us. |
| Properties / Main use conditions - Excellent resistance to corrosion in alkaline atmospheres and acid reducing atmospheres. Good resistance in mineral acids in confined atmospheres. A rare metal which resists to caustic soda, concentrated (about 50%) and hot (about 150°C). Good mechanical properties in a large range of temperatures. |
| Applications - Acid or alkaline food production (fruit juices, ice-creams), cristallization and concentration of mineral salts. Concentration of caustic salts. Machineries in which hydrocarbons are in reaction with fluorides. Storing and carriage of phenol. Production of soaps and detergents. |
| Equivalent Grade - N02200, 2.4066, Ni.99.2, 3076(NA11), Nickel 99.2 |
Nickel 200 - Detail
Acid or alkaline food production (fruit juices, ice-creams), cristallization and concentration of mineral salts. Concentration of caustic salts. Machineries in which hydrocarbons are in reaction with fluorides. Storing and carriage of phenol. Production of soaps and detergents.
Product shapes we supply: