Stainless steel forgings for pressure vessels
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.04 | 0.10 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.040 | ||
| S | - | 0.030 | ||
| Cr | 17.00 | 20.00 | ||
| Ni | 9.00 | 13.00 | ||
| Mo | - | - | ||
| Ti | 4×C％ | 0.60 |
Stainless steel forgings for pressure vessels
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 938 (≥) | 814 (≥) | 44 | 31 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 112 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 535 (≥) | 147 (≥) | 21 | 12 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 331 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 354 | 794 | 918 |
We can customize the production of STSF321H grade, contact us for the best solution.