Carbon tool steel products which include hot or cold finished bar, plate, sheet, rod, wire, or forgings, which are normally fabricated into tools, dies, or fixtures.
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.85 | 1.50 | ||
| Mn | 0.10 | 0.40 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Si | 0.10 | 0.40 | ||
| Ni | - | 0.20 | ||
| Cr | - | 0.15 | ||
| Mo | - | 0.10 | ||
| Cu | - | 0.20 | ||
| V | 0.15 | 0.35 | ||
| W | - | 0.15 |
T72301
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 952 (≥) | 189 (≥) | 24 | 24 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 965 (≥) | 193 (≥) | 33 | 33 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 978 | 174 | 878 |
We can customize the production of W2-A grade, contact us for the best solution.