Used in the products of the automobile, truck, tractor, and allied industries
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | - | 3.50 | ||
Si | 1.30 | 1.80 | ||
Mn | 0.60 | 0.90 | ||
P | - | 0.15 | ||
S | - | 0.12 |
F10011
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
392 (≥) | 563 (≥) | 41 | 31 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 123 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
469 (≥) | 726 (≥) | 34 | 22 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 324 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
758 | 259 | 257 |
We can customize the production of F10011 grade, contact us for the best solution.