Austenitic Chromium Manganese Copper Molybdenum Stainless Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.15 | ||
| Si | - | 1.00 | ||
| Mn | 17.0 | 19.0 | ||
| P | - | 0.045 | ||
| S | - | 0.03 | ||
| Cr | 17.0 | 19.0 | ||
| Mo | 0.75 | 1.25 | ||
| Cu | 0.75 | 1.25 | ||
| N | 0.40 | 0.60 |
S28200
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 789 (≥) | 276 (≥) | 22 | 11 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 432 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 267 (≥) | 733 (≥) | 32 | 33 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 173 | 773 | 467 |
We can customize the production of S28200 grade, contact us for the best solution.