| C(％) | Si(％) | Mn(％) | P(％) | S(％) |
|---|---|---|---|---|
| 0.42～0.48 | 0.17～0.37 | 0.50～0.80 | 0.030 | 0.030 |
Delivery hardness HBS: 155 ~ 210
The recommended heat treatment system: 850 ℃ to + 560 ℃ oil cold air cooling
σ b frequency/MPa: 600
σ s frequency/MPa: 355
δ 5 (%) frequency: 16
AKU frequency/J (1) : 35
| Proof strength Rp0.2(MPa) |
Tensile strength Rm(MPa) |
Impact energy KV(J) |
Elongation at fracture A(%) |
Reduction in cross section on fracture Z(%) |
As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 851(≥) | 145(≥) | 12 | 44 | 12 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 341 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J/kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 694(≥) | 573(≥) | 42 | 11 | 43 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 431 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0)N/mm2 |
Creep rupture strength (10000h) (Rp1,0)N/mm2 |
|||||
| 145 | 836 | 882 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |