Hot-Work Tool Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.32 | 0.45 | ||
| Si | 0.20 | 0.50 | ||
| Mn | 0.20 | 0.50 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Cr | 4.00 | 4.75 | ||
| Mo | 0.30 | 0.55 | ||
| V | 1.75 | 2.20 | ||
| W | 3.75 | 4.50 | ||
| Ni＋Cu | - | 0.75 | ||
| Co | 4.00 | 4.50 |
Hot-Work Tool Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 546 (≥) | 193 (≥) | 14 | 44 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 241 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 588 (≥) | 654 (≥) | 24 | 34 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 233 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 117 | 673 | 818 |
We can customize the production of T20819 grade, contact us for the best solution.