Valve steels and alloys for internal combustion engines
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.48 | 0.58 | ||
| Si | - | 0.45 | ||
| Mn | 8.00 | 10.00 | ||
| P | - | 0.045 | ||
| S | - | 0.030 | ||
| Cr | 20.00 | 22.00 | ||
| Ni | 3.25 | 4.50 | ||
| Mo | - | - | ||
| N | 0.38 | 0.50 | ||
| C+N | 0.90 | - |
Valve steels and alloys for internal combustion engines
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 343 (≥) | 445 (≥) | 41 | 13 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 322 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 765 (≥) | 929 (≥) | 24 | 43 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 421 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 574 | 627 | 899 |