Valve seat insert information
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.40 | ||
| Si | - | 0.90 | ||
| Mn | - | 0.30 | ||
| P | - | - | ||
| S | - | - | ||
| Ni | - | - | ||
| Cr | - | 5.00 | ||
| Al | - | - | ||
| Cu | - | - | ||
| Ti | - | - | ||
| Fe | - | remaining | ||
| Mo | - | 1.30 | ||
| Co | - | - | ||
| V | - | 0.50 |
Valve seat insert information
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 955 (≥) | 519 (≥) | 33 | 31 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 234 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 321 (≥) | 411 (≥) | 44 | 24 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 424 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 627 | 667 | 314 |
We can customize the production of EH-11 grade, contact us for the best solution.