Austenitic Chromium Manganese Nickel Silicon Stainless Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.15 | ||
| Mn | 4.00 | 6.00 | ||
| Si | 3.00 | 4.00 | ||
| P | - | 0.04 | ||
| S | - | 0.04 | ||
| Cr | 15.00 | 18.00 | ||
| Ni | 4.00 | 6.00 | ||
| Mo | - | 0.50 | ||
| N | 0.08 | 0.20 |
Austenitic Chromium Manganese Nickel Silicon Stainless Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 628 (≥) | 211 (≥) | 31 | 23 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 342 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 732 (≥) | 136 (≥) | 33 | 31 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 221 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 583 | 732 | 326 |
We can customize the production of S20161 grade, contact us for the best solution.