Stainless steels - Part 3: Technical dStainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposeselivery conditions for semi-finishe
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.95 | 1.20 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.040 | ||
| S | - | 0.015 | ||
| Cr | 16.0 | 18.0 | ||
| Mo | 0.40 | 0.80 |
Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 642 (≥) | 463 (≥) | 13 | 33 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 242 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 944 (≥) | 491 (≥) | 31 | 11 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 224 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 952 | 368 | 247 |
We can customize the production of X105CrMo17 grade, contact us for the best solution.