Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.12 | ||
| Si | - | 0.80 | ||
| Mn | - | 0.70 | ||
| P | - | 0.015 | ||
| S | - | 0.012 | ||
| Cr | 19.00 | 22.00 | ||
| Ni | - | remaining | ||
| Mo | - | - | ||
| Al | - | 0.15 | ||
| Ti | 0.15 | 0.35 | ||
| Fe | - | 1.00 |
Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 916 (≥) | 928 (≥) | 31 | 24 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 113 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 195 (≥) | 597 (≥) | 21 | 41 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 322 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 831 | 249 | 257 |
We can customize the production of XH78T grade, contact us for the best solution.