Hot-Work Tool Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.30 | 0.40 | ||
| Si | 0.15 | 0.30 | ||
| Mn | 0.20 | 0.40 | ||
| Cr | 3.00 | 3.75 | ||
| Mo | - | - | ||
| V | 0.30 | 0.50 | ||
| W | 8.75 | 10.00 |
Hot-Work Tool Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 895 (≥) | 312 (≥) | 23 | 34 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 166 (≥) | 638 (≥) | 42 | 12 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 391 | 156 | 836 |
We can customize the production of H21 grade, contact us for the best solution.