Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.08 | 0.14 | ||
| Si | - | 0.50 | ||
| Mn | - | 0.50 | ||
| P | - | 0.015 | ||
| S | - | 0.010 | ||
| Cr | 9.00 | 12.00 | ||
| Ni | - | remaining | ||
| Mo | 4.00 | 6.00 | ||
| Al | 3.70 | 4.70 | ||
| Ti | 2.00 | 2.80 | ||
| Fe | - | 5.00 | ||
| Co | 14.00 | 16.00 | ||
| W | 5.00 | 7.00 | ||
| V | 0.20 | 0.80 | ||
| B | - | 0.020 |
Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 275 (≥) | 432 (≥) | 43 | 12 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 754 (≥) | 217 (≥) | 22 | 13 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 124 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 315 | 991 | 555 |
We can customize the production of XH50BMTKΦЮ(ЭП57) grade, contact us for the best solution.