Martensitic Stainless Steel Bars for High-Temperature Service
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.05 | ||
| Mn | 0.50 | 1.00 | ||
| Si | - | 0.05 | ||
| P | - | 0.02 | ||
| S | - | 0.005 | ||
| Cr | 12.00 | 14.00 | ||
| Ni | 4.00 | 7.00 | ||
| Mo | 0.50 | 1.00 | ||
| N | 0.06 | 0.12 |
Martensitic Stainless Steel Bars for High-Temperature Service
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 917 (≥) | 867 (≥) | 12 | 13 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 233 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 323 (≥) | 873 (≥) | 21 | 24 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 342 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 431 | 523 | 188 |
We can customize the production of A 565 S41425 grade, contact us for the best solution.