Precipitation Hardenable Chromium Nickel Aluminum Molybdenum Stainless Steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.05 | ||
| Mn | - | 0.20 | ||
| Si | - | 1.00 | ||
| P | - | 0.01 | ||
| S | - | 0.008 | ||
| Cr | 12.25 | 13.00 | ||
| Ni | 7.50 | 8.50 | ||
| Mo | 2.00 | 2.50 | ||
| Al | 0.90 | 1.35 | ||
| N | - | 0.01 |
Precipitation Hardenable Chromium Nickel Aluminum Molybdenum Stainless Steel
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 219 (≥) | 253 (≥) | 42 | 42 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 434 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 467 (≥) | 147 (≥) | 32 | 43 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 222 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 964 | 114 | 737 |
We can customize the production of S13800 grade, contact us for the best solution.