Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.12 | ||
| Si | - | 0.60 | ||
| Mn | 1.00 | 2.00 | ||
| P | - | 0.030 | ||
| S | - | 0.020 | ||
| Cr | 14.00 | 16.00 | ||
| Ni | 34.00 | 38.00 | ||
| Mo | - | - | ||
| Al | - | - | ||
| Ti | 1.10 | 1.50 | ||
| Fe | - | - | ||
| W | 2.80 | 3.50 |
Russia GOCT standard deformation of high temperature alloy grades and chemical composition
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 324 (≥) | 691 (≥) | 13 | 42 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 221 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 173 (≥) | 345 (≥) | 34 | 21 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 323 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 291 | 882 | 414 |
We can customize the production of XH35BT grade, contact us for the best solution.