Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.13 | 0.20 | ||
| Cr | 9.50 | 12.00 | ||
| Ni | - | remaining | ||
| Co | 4.00 | 5.50 | ||
| Mo | 3.50 | 4.50 | ||
| W | 4.50 | 5.50 | ||
| Al | 5.00 | 6.00 | ||
| Ti | 2.50 | 3.20 | ||
| Nb | - | - | ||
| Fe | - | 2.00 |
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 371 (≥) | 473 (≥) | 33 | 24 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 144 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 695 (≥) | 739 (≥) | 12 | 41 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 332 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 612 | 198 | 523 |
We can customize the production of ЖC6K-BИ grade, contact us for the best solution.