Wrought steels for use at elevated temperatures in engines
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.36 | 0.44 | ||
| Si | 0.15 | 0.35 | ||
| Mn | 0.45 | 0.85 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Cr | 0.90 | 1.20 | ||
| Mo | 0.55 | 0.75 | ||
| Ni | - | - | ||
| V | 0.25 | 0.35 |
Wrought steels for use at elevated temperatures in engines
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 559 (≥) | 187 (≥) | 44 | 31 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 529 (≥) | 625 (≥) | 42 | 21 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 121 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 911 | 126 | 624 |
We can customize the production of 40CrMoV4-6 grade, contact us for the best solution.