Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.11 | 0.17 | ||
| Cr | 12.00 | 15.00 | ||
| Ni | - | remaining | ||
| Co | - | - | ||
| Mo | 12.00 | 15.00 | ||
| W | 8.00 | 10.00 | ||
| Al | 1.50 | 3.00 | ||
| Ti | 2.00 | 3.20 | ||
| Nb | - | - | ||
| Fe | - | - |
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 367 (≥) | 918 (≥) | 11 | 42 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 883 (≥) | 567 (≥) | 14 | 11 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 264 | 377 | 914 |
We can customize the production of BЖЛ2-BИ grade, contact us for the best solution.