High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.15 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.035 | ||
| S | - | 0.030 | ||
| Ni | 8.00 | 10.00 | ||
| Cr | 17.00 | 19.00 |
1Cr18Ni9
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 967 (≥) | 996 (≥) | 14 | 11 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 343 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 369 (≥) | 325 (≥) | 33 | 13 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 111 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 842 | 913 | 852 |
We can customize the production of 1Cr18Ni9 grade, contact us for the best solution.