Nickel Alloy, Corrosion and Heat-Resistant, Investment Castings 52Ni - 19Cr - 11Co - 9.8Mo - 3.2Ti - 1.6Al - 0.006B Vacuum-Melted, Vacuum-Cast, Solution Heat Treated
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.09 | ||
| Si | - | 0.25 | ||
| Mn | - | 0.25 | ||
| Cr | - | 19.00 | ||
| Ni | - | remaining | ||
| Mo | - | 10.00 | ||
| Co | - | 11.00 | ||
| W | - | - | ||
| Al | - | 1.50 | ||
| Cu | - | - | ||
| Ti | - | 3.10 | ||
| Fe | - | 1.80 | ||
| B | - | 0.005 |
Nickel Alloy, Corrosion and Heat-Resistant, Investment Castings 52Ni - 19Cr - 11Co - 9.8Mo - 3.2Ti - 1.6Al - 0.006B Vacuum-Melted, Vacuum-Cast, Solution Heat Treated
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 364 (≥) | 786 (≥) | 23 | 33 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 132 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 258 (≥) | 947 (≥) | 22 | 22 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 528 | 855 | 899 |
We can customize the production of Rene 41 grade, contact us for the best solution.