Iron and steel. Stainless steel for high temperature application
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.08 | 0.13 | ||
| Si | - | 0.40 | ||
| Mn | 0.50 | 0.90 | ||
| P | - | 0.030 | ||
| S | - | 0.025 | ||
| Cr | 11.00 | 12.50 | ||
| Ni | 2.00 | 4.00 | ||
| N | 0.020 | 0.040 | ||
| V | 0.25 | 0.40 |
Z 12 CNDV 12-03 is a new type of martensitic stainless steel for the last-stage blades of large-capacity nuclear and thermal power turbines. The deformation behavior of this steel was studied by thermal compression experiments that performed on a Gleeble-3500 thermal simulator at a temperature range of 850°C to 1200°C and a strain rate of 0.01s-1 to 20s-1. When the deformation was performed at high temperature and low strain rate, a necklace type of microstructures was observed, the plastic deformation mechanism is grain boundary slip and migration, when at low temperature and lower strain rate, the slip bands were observed, the mechanism is intracrystalline slips, and when at strain rate of 20s-1, twins were observed, the mechanism are slips and twins. The Arrhenius equation was applied to describe the constitutive equation of the flow stress. The accuracy of the equation was verified by using the experimental data and the correlation coefficient R2 = 0.9786, and the equation can provide reasonable data for the design and numerical simulation of the Z12CNDV12-03 forging process.
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 175 (≥) | 379 (≥) | 13 | 34 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 123 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 899 (≥) | 854 (≥) | 41 | 22 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 224 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 489 | 774 | 713 |
We can customize the production of Z12CNDV12-03 grade, contact us for the best solution.