Seamless Austenitic Steel Pipe for High-Temperature Central-Station Service
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.08 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.045 | ||
| S | - | 0.03 | ||
| Cr | 16.0 | 18.0 | ||
| Ni | 10.0 | 14.0 | ||
| Mo | 2.00 | 3.00 | ||
| N | 0.10 | 0.16 |
Seamless Austenitic Steel Pipe for High-Temperature Central-Station Service
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 745 (≥) | 993 (≥) | 42 | 33 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 211 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 716 (≥) | 742 (≥) | 33 | 42 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 868 | 775 | 454 |
We can customize the production of A 376 TP316N grade, contact us for the best solution.