Used in the products of the automobile, truck, tractor, and allied industries. Miscellaneous soft iron castings (as cast or annealed) in which strength is not of primary consideration. Exhaust manifolds may be made of this grade of iron, alloyed or unallo
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 3.40 | 3.70 | ||
| Si | 2.30 | 2.80 | ||
| Mn | 0.50 | 0.80 | ||
| P | - | 0.25 | ||
| S | - | 0.15 | ||
| CEV | 4.25 | 4.5 |
F10004
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 968 (≥) | 416 (≥) | 13 | 32 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 443 (≥) | 758 (≥) | 24 | 22 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 113 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 177 | 573 | 598 |
We can customize the production of F10004 grade, contact us for the best solution.