Steel, Maraging, Bars, Forgings, Tubing, and Rings 18.5Ni - 9.0Co - 4.9Mo - 0.65Ti - 0.10Al Consumable Electrode Vacuum Melted, Annealed
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.03 | ||
| Si | - | 0.10 | ||
| Mn | - | 0.10 | ||
| Ni | - | 18.00 | ||
| Cr | - | - | ||
| Al | - | 0.10 | ||
| Cu | - | - | ||
| Ti | - | 0.40 | ||
| Fe | - | - | ||
| Mo | - | 5.00 | ||
| Co | - | 8.00 |
Steel, Maraging, Bars, Forgings, Tubing, and Rings 18.5Ni - 9.0Co - 4.9Mo - 0.65Ti - 0.10Al Consumable Electrode Vacuum Melted, Annealed
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 888 (≥) | 144 (≥) | 41 | 14 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 124 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 174 (≥) | 971 (≥) | 12 | 32 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 144 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 622 | 848 | 235 |
We can customize the production of Marage 300 grade, contact us for the best solution.