Steel for intake valves
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.40 | |||
| Si | 3.90 | |||
| Mn | 0.30 | |||
| P | ||||
| S | ||||
| Cr | 2.20 |
Steel for intake valves
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 995 (≥) | 238 (≥) | 22 | 14 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 457 (≥) | 816 (≥) | 22 | 31 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 442 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 335 | 121 | 557 |