Steel for intake valves
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.40 | |||
| Si | 3.90 | |||
| Mn | 0.30 | |||
| P | ||||
| S | ||||
| Cr | 2.20 |
Steel for intake valves
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 538 (≥) | 254 (≥) | 11 | 14 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 224 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 886 (≥) | 474 (≥) | 23 | 44 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 696 | 537 | 848 |
We can customize the production of S64006 grade, contact us for the best solution.