Valve steels and alloys for internal combustion engines
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.04 | 0.10 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.030 | ||
| S | - | 0.015 | ||
| Cr | 18.00 | 21.00 | ||
| Ni | - | remaining | ||
| Mo | - | - | ||
| Al | 0.30 | 1.00 | ||
| Ti | 1.00 | 2.00 | ||
| Fe | 23.00 | 28.00 | ||
| B | - | 0.008 | ||
| Nb+Ta | 1.00 | 2.00 |
Valve steels and alloys for internal combustion engines
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 464 (≥) | 784 (≥) | 42 | 34 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 234 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 243 (≥) | 351 (≥) | 12 | 11 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 114 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 174 | 582 | 723 |
We can customize the production of 2.4955 grade, contact us for the best solution.
–sales@specificsteel.com