| 1.4435 |
Germany AWS |
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| X2CrNiMo18-14-3 |
Germany AWS |
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| 00Cr17Ni14Mo2 |
China GB |
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| S20103 |
USA AISI |
Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| 201L |
USA YB |
Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| S20100 |
USA AISI |
Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| SA 201 |
USA SAE |
Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| 201 |
USA YB |
Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| 0Cr18Ni12Mo2Ti |
China GB |
Seamless stainless steel tubes for boiler and heat exchanger |
| 1Cr18Ni12Mo2Ti |
China GB |
Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr17Ni12Mo2 |
China GB |
Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr25Ni20 |
China GB |
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel |
| 0Cr23Ni13 |
China GB |
Corrosion resistance and heat resistance are better than 0cr19ni9 |
| 1Cr18Ni12 |
China GB |
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading |
| 00Cr18Ni10N |
China GB |
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance |
| 0Cr19Ni10NbN |
China GB |
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES |
| 0Cr19Ni9N |
China GB |
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components |
| 1Cr18Mn8Ni5N |
China GB |
Nickel steel, instead of 1cr18ni9 |
| 1Cr17Mn6Ni5N |
China GB |
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc |
| 00Cr19Ni10 |
China GB |
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts |
| 0Cr18Ni9 |
China GB |
Seamless stainless steel tubes for boiler and heat exchanger |
| Y1Cr18Ni9Se |
China GB |
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws |
| 1Cr17Ni7 |
China GB |
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc |
| 1Cr18Mn10Ni5Mo3N |
China GB |
Of urea with good corrosion resistance, can produce urea corrosion of the equipment. |
| 1Cr18Ni9 |
China GB |
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts |
| Y1Cr18Ni9 |
China GB |
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut |